۱Synthesis and characterization of gelatin based scaffold with 1 sufficient mechanical properties for bone implant
اطلاعات انتشار: اولین کنفرانس بین المللی دستاوردهای نوین پژوهشی در مکانیک، مکاترونیک و بیومکانیک ، سال
تعداد صفحات: ۸
In the current study freeze casting method was employed to fabricate highly porous gelatin\ akermanite scaffolds. 10 Gelatin(GEL) based nanocomposite scaffolds were prepared a controlled unidirectional freeze casting through blending constant gelatin concentration with Akermanite nanoparticles (AKRNPs). Pore morphology, mechanical properties, and water adsorption characteristics of scaffolds were assessed. The compressive strength and elastic module values was 5.46 MPa, and 2.86 GPa, respectively. Scanning Electron Microscopy (SEM) images depicted a unidirectional structure with homogenous distribution of AKR among gelatin matrix.<\div>