۱Electrical and electrochemical properties of expanded graphite filled polythiophene nanocomposites
اطلاعات انتشار: Scientia Iranica، بيست و دوم،شماره۶، ۲۰۱۵، سال
تعداد صفحات: ۸
In this study, graphite nanosheets were prepared by powdering expanded graphite with sonication in aqueous alcoholic solution. A facile process for the synthesis of expanded graphite filled polythiophene (PTh\EG) conducting composites was developed. The nanocomposites were fabricated via chemical polymerization of thiophene monomer in the presence of expanded graphite nanosheets in various proportions. Nanocomposites were characterized by Fourier transform infrared spectroscopy (FT–IR), scanning electron microscopy (SEM), Scanning Tunneling Microscopy (STM), X–ray diffraction (XRD), cyclic voltammetry (CV) and electrical conductivity measurements. . SEM observations from cross–sections of EGwere performed to understand the microstructure occurrence during interpenetration.Electrical conductivity of PTh\EG was notably enhanced by the introduction of EG. The composite exhibited good electrical conductivity of 125 Scm–1 when the EG content was 0.5 wt %. CV is the most commonly used technique for evaluation of electrochemical properties of a film on the electrode surface.The composites also showed excellent electrochemical reversibility at the scan rate of 50 mVs–1 and maximum reversible electrochemical response was almost unchanged even up to 100 cycles. The stability of oxidation and reduction peaks of nanocomposites in cyclic voltammetry up to 100 cycles show that obtained nanocomposites are very appropriate to be used in rechargeable batteries.
نمایش نتایج ۱ تا ۱ از میان ۱ نتیجه